When installing the roll coating after gluing it to the base,

For use immiately it is strongly recommend to completely exclude any mechanical impacts on the surface for at least 12 hours.

The modular coating theoretically europe cell phone number list allows , but when using additional adhesive fasteners, it is also necessary to maintain drying time intervals

For use immiately in accordance with the manufacturer’s technical recommendations.

Step-by-step technology for laying self-leveling

Rubber coating Preparation of components for self-leveling rubber coating requires special care,

since the quality of the final result directly jointly promote the expansion of hong kong’s motor insurance market depends on the correct ratio of ingrients.

Rubber crumb must be dry, without impurities and foreign inclusions, with a granule size of 1 to 4 mm for the bottom layer and 1 to 3 mm for the top layer.

The polyurethane binder must be thoroughly mix before use to ensure homogeneity of the composition.

Color pigments are add in strictly

Defin proportions to achieve the desir shade of the coating.

All components must have a temperature mobile lead of at least +15°C to ensure optimal curing conditions for the mixture.

The components are mix in a special mixer with forc mixing, which allows for uniform distribution of the binder throughout the entire volume of rubber crumb.

For the lower (base) layer of the coating, the optimal ratio is 15-20% of the polyurethane binder by weight of the rubber crumb.

For the upper (finish) layer

This ratio increases to 20-25%, which ensures higher density and wear resistance of the surface.

The mixing time of the components should be at least 5-7 minutes to achieve a homogeneous consistency of the mixture.

After mixing is complete, it is necessary to immiately begin laying the material, since the viability of the mixture is limit and ranges from 30 to 60 minutes depending on the ambient temperature.

Laying the lower (base) layer of the self-leveling coating is carri out by continuous pouring using special guides that ensure a uniform coating thickness.